Divinol Fett Top 2003
Art-Nr.: 23980
Semi-synthetic, water-repellent calcium soap grease.
extremely adhesive
wear and corrosion protection
classification KP 2 G-30 as per DIN 51 825
classification ISO-L-ISO-L-XCBIB 2 as per
ISO/DIS 6743-9
Divinol Fett Top 2003 is a versatile special grease which offers a strong adhesion due to its high base oil viscosity.
It is especially used for lubricating points with critical loads as e.g. high humidity, influence of salt-water and
impact loads.
Appearance: green fluorescent
Thickening agent: Calcium soap
Operating temperature range: -30°C - +110°C
Base oil viscosity/40°C / ASTM D 7042: 1000 mm²/s
Unworked penetration/0.1 mm / DIN ISO 2137: 270
Worked penetration/0.1mm, 60 double strokes / DIN ISO 2137: 280
Worked penetration/0.1mm, 60 000 double strokes / DIN ISO 2137: 300
Dropping point / DIN ISO 2176: 140 °C
Water resistance / DIN 51807-1: Evaluation level 0
Corrosion protection behaviour (EMCOR-test) / DIN 51 802: 0/0
VKA welding load / DIN 51 350/T4: 2200 N
Corrosion effect on copper 24h/100°C / DIN 51 811: Corrosion degree 1
Art-Nr.: 23980
Semi-synthetic, water-repellent calcium soap grease.
extremely adhesive
wear and corrosion protection
classification KP 2 G-30 as per DIN 51 825
classification ISO-L-ISO-L-XCBIB 2 as per
ISO/DIS 6743-9
Divinol Fett Top 2003 is a versatile special grease which offers a strong adhesion due to its high base oil viscosity.
It is especially used for lubricating points with critical loads as e.g. high humidity, influence of salt-water and
impact loads.
Appearance: green fluorescent
Thickening agent: Calcium soap
Operating temperature range: -30°C - +110°C
Base oil viscosity/40°C / ASTM D 7042: 1000 mm²/s
Unworked penetration/0.1 mm / DIN ISO 2137: 270
Worked penetration/0.1mm, 60 double strokes / DIN ISO 2137: 280
Worked penetration/0.1mm, 60 000 double strokes / DIN ISO 2137: 300
Dropping point / DIN ISO 2176: 140 °C
Water resistance / DIN 51807-1: Evaluation level 0
Corrosion protection behaviour (EMCOR-test) / DIN 51 802: 0/0
VKA welding load / DIN 51 350/T4: 2200 N
Corrosion effect on copper 24h/100°C / DIN 51 811: Corrosion degree 1